Automatic Leak Detection Debinding Sintering Furnace Vacuum Partial Pressure

Valid working space(W*H*L)

The vacuum degree can reach 5Pa within 30min after starting the pump. After reaching 5Pa and then pumping for 30min, the ultimate vacuum value reaches 1Pa (within a cold, empty and clean furnace that has been dried before).

≤3Pa/h (stop the pump group operation and start checking after testing the limit vacuum (within a cold, empty and clean furnace that has been dried before).

≤7h(full load,from 1450℃cooling down to 100℃,water temperature≤26℃,2 bar≤water pressure≤3bar)

It's equipped with air cooler for rapid cooling that can also cool the furnace.

About 400KVA (The output power can be limited)

8℃/min (the room temperature rises to 1450℃within a vacuum and empty furnace. 600℃, 1000℃, 1200℃ half-way insulation is allowed).

≥98%(10kg pure paraffin, argon negative pressure dewaxing. Measured by three times of mean values at most).

UPS guarantee time

It can power the indicator light and control the furnace during power outage for more than 80 minutes.

Atmosphere Uniformity in sintering zone

Positive pressure or negative pressure degreasing integration sintering uniformity:

furnace control piece (YC40 or YG6 particles) and paraffin forming agent are evenly distributed on the graphite boat.

*(The buyer shall provide the furnace control piece and program, and the seller shall confirm.)

Alnico: test cobalt magnetic field after dewaxing, deviation range: ≤±0.3%; Coercive force: deviation range: ≤± 0.4kA /M. The uniformity of furnace temperature is the standard of the uniformity of coercive force.